عنوان انگلیسی: Effect of oxygen vacancy sites on CO2 adsorption dynamics: The case of rutile (1 · 1)-TiO2 (110)

عنوان فارسی: اثر سایت های خالی اکسیژن بر دینامیک جذب CO2: مورد روتایل (1 1) -TiO2 (110)

نام ژورنال: Chemical Physics Letters

سال انتشار: 2006

تعداد صفحات مقاله انگلیسی:5

تعداد صفحات ترجمه فارسی:13

Abstract
The adsorption of CO2 has been studied by molecular beam scattering on slightly and strongly reduced TiO2(110). The defect density
has qualitatively been characterized by CO2 TDS. Two peaks are present in TDS, which can be assigned to CO2 adsorption on pristine
and oxygen vacancy sites. Interestingly, the initial reactivity, S0, towards CO2 adsorption decreases with increasing defect density and
increases with increasing oxygen preexposure. The latter is related to the vanishing of the defect structure in TDS. In contrast, hydrogen
preexposure leads to a decrease in S0 as well as the intensity of both TDS peaks decrease in sympathy.

چکیده

جذب CO2 توسط پراکندگی پرتو مولکولی در TiO2 (110) کم و به شدت کاهش یافته مطالعه شده است. نقص دانسیته به لحاظ کیفی توسط TDS CO2 مشخص شده است. دو پیک در TDS، حاضر است که می توانند به جذب CO2 در سایت های خالی و بکر اکسیژن اختصاص داده شوند. جالب توجه است، واکنش اولیه، S0، به سمت جذب CO2 با افزایش نقص دانسیته کاهش می یابد و با افزایش اکسیژن از پیش در معرض قرار گرفته افزایش می یابد. در حالت دوم به محو ساختار نقص در TDS مربوط می شود. در مقابل، هیدروژن از پیش در معرض گرفته منجر به کاهش در S0 می شود و همچنین شدت TDS پیک ها را در همبستگی کاهش می دهد.