Formation and Mechanical Properties of New Cu-Rich Cu-Zr-Al-Ag Glassy Alloys with High Glass-Forming Ability

عنوان فارسی: فرمولاسیون و خواص مکانیکی آلیاژهای شیشه ایجدید Cu-Zr-Al-Ag غنی از Cu با توانایی بالا تشکیل شیشه ای

نام ژورنال: MATERIALS TRANSACTIONS

سال انتشار: ،2009

تعداد صفحات مقاله انگلیسی: 4

تعداد صفحات ترجمه فارسی: 12

We have discovered new Cu-rich Cu-Zr-Al-Ag bulk glassy alloys with high glass-forming ability and excellent mechanical properties. As the composition shifted to Cu-rich range in the Cu_46+xZr_46−xAg₄Al₄ alloy series, the supercooled liquid region, reduced glass transition temperature and γ value increased, leading to the improvement of the GFA. The full glassy samples with a diameter of 10 mm could be fabricated by copper mold casting for the Cu_46+xZr_46−xAg₄Al₄ (x=1–3) alloys. In addition to high GFA, the BGAs exhibit good mechanical properties under a compressive deformation mode, i.e., large Young’s modulus of 104–109 GPa, high fracture strength of 1905–1932 MPa and distinct plastic strain of 0.2–0.4%.

ما آلیاژهای شیشه ای بالک Cu-Zr-Al-Ag غنی از Cu را با توانایی بالای ساخت شیشه ای و خواص مکانیکی عالی کشف کرده ایم.همانطور که ترکیب به محدوده غنی از Cu در سری آلیاژ منتقل شده است، منطقه مایع فوق خنک، دمای انتقال شیشه را کاهش می دهد و مقدار γ افزایش یافته است، که منجر به بهبود GFA می شود.نمونه های کامل شیشه ای با قطر 10 میلی متر می تواند توسط ریخته گری قالب های مس برای آلیاژهای ساخته شود.علاوه بر GFA بالا، BGA ها دارای خواص مکانیکی خوبی در یک حالت تغییر شکل فشاری هستند، به عنوان مثال، مدول بزرگ یانگ 104-109 GPa، مقاومت در برابر شکست بالا 1932-1393 مگاپاسکال و کشش پلاستیکی متمایز از 0.2-0.4٪ نمایش می دهند.